ASTM E208 Drop Weight Test for Nil-Ductility Temperature of Ferritic Steel
The ASTM E208 drop weight test is used to determine the nil-ductility transition (NDT) temperature of ferritic steels 5/8 inch thick (15.9 mm) and over. The NDT temperature is the temperature at which the fracture mode of steel changes from ductile to brittle. At temperatures above the NDT a piece of steel will stretch or deform in a ductile manner before fracturing when loaded to its ultimate tensile strength. At temperatures lower than the NDT that same piece of steel will fail in a brittle manner when loaded to its yield strength (roughly half of its ultimate tensile strength). Once a brittle failure begins the crack will continue to grow until it runs out of material, the pressure is released or it encounters steel that is more ductile.
To find out the steel’s NDT temperature, beam specimens are prepared according to ASTM E208 and subjected to a single impact from a drop weight test system. The Ceast falling weight tester Model 9350 is suitable for this test. This model is capable of testing specimens with an impact energy from 0.59 – 757 J (0.44 to 558 ft-lb). It is capable of testing type P2 specimens 19 x 130 x 50 mm (0.75” x 5” x 2”) and type P3 specimens 16 x 130 x 50 mm (0.62” by 5” by 2”). When coupled with the DAS 64K Data Acquisition System, a full load - time - displacement - energy data curve and tests results can be captured for each test through the VisualImpact module from the CeastView software.
Impact resistance is one of the most important properties for component designers to consider, as well as the most difficult to quantify. Impact resistance is a critical measure of service life and more importantly these days, it involves the perplexing problem of product safety and liability. With the combined experience of Dynatup® and CEAST, Instron® has more than 80 years experience in designing impact testing systems to simulate real-life impact conditions.
- 1.7 MB